Impact du broyage des granulats de PET sur les propriétés à l'état frais d'un composite cimentaire
Résumé
The works presented herein deal with the recycling of post-consumer packaging made of polyethylene terephthalate (PET) without further transformation beyond crushing. Several crushers are used to obtain PET aggregates with different sizes. The PET particles are substituted to sand according a same volume fraction. 25, 50 and 75% are the substitution rates chosen. Each composition contains only one type of PET grain size. Optical imaging has allowed to observe that the 2 mm-crushed PET exhibited lots of fine particles. Moreover the water absorption rate of industrial PET is lower than 2 mm-crushed PET one. The Water/Cement (W/C) rate decreases with the volume percentage of industrial PET increase while this rate increases with the increase in volume percentage of 2 mm-crushed PET.
Les travaux présentés ici portent sur la recyclabilité d'emballages de post consommation à base de polyéthylène téréphtalate (PET) avec comme seule technique de transformation le broyage. Différents broyeurs sont utilisés pour obtenir des granulats de PET de différentes tailles. Les particules de PET ont été substituées au sable selon une même fraction volumique. Les taux de substitution choisis sont 25, 50 et 75%. Un seul type de granulométrie de PET a été utilisé dans chaque composition. On a observé par imagerie optique que le PET broyé à 2 mm présentait beaucoup de fines particules. De plus l'absorption d'eau du PET industriel est plus faible que celle du PET broyé à 2 mm. Le rapport Eau/Ciment (E/C) diminue lorsque le pourcentage volumique du PET industriel augmente tandis que ce rapport augmente avec l'augmentation du pourcentage volumique du PET broyé à 2 mm.
| Origine | Fichiers produits par l'(les) auteur(s) |
|---|
Loading...